Spin-Coatable Clear Reprographic Silicone, 1.01 kg Kit

Cat No:SRE-0084

Description

A dilute, flexible and clear silicone formulation designed for forming submicron reprographic silicone films by spin coating.

Datasheet

Inquiry

Basic Information

Appearance	Clear
Viscosity	1-2 cSt, solution and mixed
Specific Gravity	0.71
Refractive Index	1.43 at 25 degrees C
Flash Point	-4 degrees C
Color	Clear
Features and Benefits	A dilute, flexible and clear silicone formulation designed for forming submicron reprographic silicone films by spin coating.
Usage Instructions	Mix the two components at the stated ratio while limiting air inclusion. De-air under vacuum for critical work, cast or coat, and cure under the listed conditions.
Packaging	1.01 kg kit: 1,000 g Part A and 10 g Part B
Solid Content	8-12 wt%
Working Time	12 hours at 25 degrees C
Curing Conditions	80 degrees C for 4 hours or room temperature for 36 hours
Shore A Hardness	45-60
Tensile Strength	5.5-7.0 MPa
Elongation at Break	80-100%
Tear Strength	1.75-2.60 kN/m
Relative Permittivity	2.7
Product Standard	nan
PID Resistance	nan
Component System	Two-part system
Mix Ratio	100:1
Cure Type	Platinum-catalyzed addition cure
Part A Viscosity	1-2 cSt
Part B Viscosity	50-75 cSt
Critical Surface Tension	23-24 mN/m
Contact Angle (Water)	105-110 degrees
Recommended Spin Speed	1,000-2,000 rpm for submicron films

Applications

Submicron silicone thin films; spin-coated microfluidic and soft-lithography structures.