Low-Volatility Reprographic Silicone for Stable Microdevices, 100 g Kit

Cat No:SRE-0082

Description

A flexible clear, high-definition silicone compound with low volatile content, improved dimensional stability, lower extractables and slower hydrophobic recovery.

Datasheet

Inquiry

Basic Information

Appearance	Clear
Viscosity	3,500-5,000 cSt, mixed
Specific Gravity	1.04
Refractive Index	1.43 at 25 degrees C
Color	Clear
Volatile Content	No more than 0.2 wt% after 4 hours at 150 degrees C
Features and Benefits	A flexible clear, high-definition silicone compound with low volatile content, improved dimensional stability, lower extractables and slower hydrophobic recovery.
Usage Instructions	Mix the two components at the stated ratio while limiting air inclusion. De-air under vacuum for critical work, cast or coat, and cure under the listed conditions.
Packaging	100 g premeasured mixing-cup kit
Working Time	12 hours at 25 degrees C
Curing Conditions	80 degrees C for 4 hours or room temperature for 36 hours
Shore A Hardness	45-60
Tensile Strength	5.5-7.0 MPa
Elongation at Break	80-100%
Tear Strength	1.75-2.60 kN/m
Relative Permittivity	2.7
Product Standard	nan
PID Resistance	nan
Component System	Two-part system
Mix Ratio	10:1
Cure Type	Platinum-catalyzed addition cure
Part A Viscosity	5,000-6,000 cSt
Part B Viscosity	50-75 cSt
Critical Surface Tension	23-24 mN/m
Contact Angle (Water)	105-110 degrees

Applications

Microelectronic and medical microdevices; long-term surface-treated structures; precision molding and encapsulation.

GET IT!

Eata Silicon delivers a diverse portfolio of silicon-based materials, from high-purity silicon and inorganic silicon compounds to functional silicon materials and customized solutions, supporting research, manufacturing, and next-generation applications across multiple industries.

For Research or Industrial Raw Materials, Not For Personal Medical Use!